DBC-402A
Product Introduction
Special polyether polyols is the main raw materials of this product, with special additives to constitute blend polyols, the characteristics are as follows,
1、good flowability in the reactivity process, the foam density distributes uniformity, with excellent dimensional stability and cohesiveness.
2、it can meet different requirements of continuous battenboard product lines
Physical Property
|
Appearance
Hydroxyl value mgKOH/g
Dynamic viscosity （25℃） mPa.S
Density （20℃） g/ml
Storage temperature ℃
Storage stability Month |
Light yellow transparent viscous liquid
300-400
150-300
1.10-1.16
10-25
6 |
Recommended Ratio
|
Raw Material |
Pbw |
|
DBC-402A blend polyols
Isocyanate |
100
100-110 |
Technology and Reactivity (the exact value varies depending on processing conditions)
|
Items |
Manual mixing |
High temperature machine |
|
Material temperature ℃
Moulding temperature ℃
Rise time s
Gel time s
Free Density kg/m3 |
25
40-45
10-20
35-65
30-35 |
25
40-45
6-15
20-40
30-35 |
Foam Performance
|
Foam density by moulding
Closed cell rate
Thermal conductivity（15℃）
Compressive Strength
(perpendicular to the direction of rising)
Dimensional Stability
（24h,-20 ℃）
（24h,100 ℃）
Flame retardance |
GB 6343
GB 10799
GB 3399
GB/T 8813
GB/T 8811
GB/T8624 |
≥40kg/m3
≥90%
≤22mW/(m.K)
≥ 100kPa
≤1.0%
≤1.5%
Level B2 |
The data provided above are typical value, which are tested by our company. For our company's products, the data included in the law do not have any constraints.